The difference between 6060 aluminum plate and 6063 aluminum plate
Sample： A4 Sized
Payment Terms： L/C,D/P,T/T
Delivery time： Within 15-30 Days
The difference between 6060 aluminum plate and 6063 aluminum plate:
The chemical composition and processing properties of 6060 aluminum plate and 6063 aluminum plate are similar, but not identical. The difference between the two is strength. 6060 is the national standard aluminum alloy for doors and windows, and 6063 is the aerospace aluminum alloy approved by the state.
6060 aluminum plate material composition:
Si: 0.3-0.6; Fe: 0.1-0.3; Cu: 0.1; Mn: 0.1; Mg: 0.35-0.6; Cr: – Zn: 0.1; Other: – Ti: 0.15; Others total: 0.15; Al: the amount.
6060 aluminum plate performance characteristics:
Tensile strength σb (MPa): ≥ 470
Conditional yield strength σ0.2 (MPa): ≥420
Elongation δ5 (%): ≥ 6
Features: 1. High strength heat treatable alloy. 2. Good mechanical properties. 3. Good usability. 4. Easy to process and good wear resistance. 5. Anti-corrosion performance, good oxidation resistance
6060 aluminum plate use:
Main uses: Aerospace fixtures, trucks, tower buildings, boats, pipelines and other areas of construction that require strength, weldability and corrosion resistance.
6063 aluminum plate chemical composition:
Aluminum Al: balance; silicon Si: 0.20-0.6; copper Cu: ≤ 0.10; magnesium Mg: 0.45-0.9; zinc Zn: ≤ 0.10; manganese Mn: ≤ 0.10; titanium Ti: ≤ 0.10; chromium Cr: ≤ 0.10; Iron Fe: 0.000 ~ 0.350; Note: single: ≤ 0.05; total: ≤ 0.15;
6063 aluminum plate product features use introduction:
6063 aluminum plate belongs to Al-Mg-Si alloy and has a wide range of applications. Especially in the construction industry, it is the most promising alloy. Good corrosion resistance, excellent weldability, good cold workability and medium strength. Mingtai Aluminum 6063 aluminum plate manufacturers are of high quality and low price.
6063 aluminum plate features application:
6063 aluminum plate The main alloying elements are magnesium and silicon. It has excellent processing properties, excellent weldability, extrusion and plating properties, good corrosion resistance, toughness, easy polishing and coloring, and excellent anodizing effect. A typical extruded alloy. 6063 aluminum plate is widely used in building profiles, irrigation pipes, vehicles, gantry, furniture, lifts, etc. due to its good plasticity, moderate heat treatment strength, good welding performance and gorgeous color on the surface after anodizing. Pipes, rods and profiles for fences and the like.
6063 aluminum plate is a low alloyed Al-Mg-Si high plasticity alloy. Has many valuable features:
1. Heat treatment strengthening, high impact toughness, and insensitivity to lack of.
2. It has excellent thermoplasticity and can be extruded at high speed into a complex structure. Thin wall. Hollow various profiles or forged forgings with complex structure, wide quenching temperature range, low quenching sensitivity, after extrusion and forging demoulding, As long as the temperature is higher than the quenching temperature. That is, it can be quenched by spraying water or water. Thin-walled parts (6<3mm) can also be subjected to wind quenching. 3. Excellent welding performance and corrosion resistance, no tendency of stress corrosion cracking. Among heat-treated reinforced aluminum alloys, Al-Mg-Si alloy is the only alloy that has no stress corrosion cracking phenomenon. 4. The surface after processing is very smooth and easy to anodize and color. The disadvantage is that if it is aged at room temperature for a period of time after quenching, it will have an adverse effect on the strength (parking effect).